FM-125 High water-proof high moisture permeability coating resin

1.Application :one component polyether type polyurethane glue resin, applied to direct coating process, to produce “breathable” waterproof and moisture fabrics.

2.Product data

Appearance: micro turbid translucent sticky liquid

solvent：DMF/TOL

viscosity(mPa·s/25℃)：40000-80000

Solid content(%)：30士2

100%modulus（kg/cm²）:30

Tensile strength(Mpa):>25

3.Property

 high moisture permeable, high waterproof property, high adhesive fastness, soft hand feeling, high anti-wear&scratch, can hot laminate PU, moisture permeable one component PU resin

4.Formula

   FM-125                  100

   Smooth agent              5

   PU white paste             20

   PA glue(25%)              8

   Polish powder             0.5-1

   Dilution solvent              X

   Process temperature:         110℃—130℃—150℃—165℃

  PS: 1. PA is used to prevent the loss of pulp. If the cloth surface is smooth, it may not be added.

2.The amount of diluted solvent (X) :It is recommended to control the wet adhesive viscosity at the operating temperature in the range of 6000~7000 (mPa·s).

5. Caution notes：1. This product should be stored in a cool, dry and ventilated place, away        

from fire, to prevent rain and damp;

2. sealed at room temperature 0 ~ 40 °C, in the winter cold resin may have freezing phenomenon, should be used after mixing

                 3. It can be stored for 6 months without change in quality

6.package：180kg/drum